10mm, 12mm, 14mm, 15mm, 16mm, 18mm, 20mm, 15mm, 30mm, 32mm, 40mm, 50mm, 60mm, 80mm, 100mm, 200mm, 500mm, 1000mm.
1inch, 2″, 3″, 4″, 5″, 8″, 10″, 20″, 30″, 40″.
Material Grade:
1.Martensitic Cr Mo AlloySteel(ZG50Cr5Mo,ZG60Cr6Mo,Cr12Mo): Hardness:≥HRC48, Impact value:≥25J.
2.High Cr white iron(BTMCr15Mo,BTMCr20Mo,BTMCr26Mo):Hardness:≥HRC56,
Impact value:≥5J.
3.Ni-hard White Iron: AS2027 NiCr2-500,AS2027 NiCr1-550,AS2027 NiCr4-500,AS2027 NiCr4-600,AS2027 NiCr4-630AS2027 NiCr2-500,AS2027 NiCr1-550,AS2027 NiCr4-500,AS2027 NiCr4-600,AS2027 NiCr4-630
Material Grades & Alloys for Wear Plates & Chute Liners:
1. High Cr white iron :
| ISO 21988/JN/ |
HBW |
C |
Si |
Mn |
P |
s |
Cr |
Ni |
Mo |
Cu |
| HBW555XCr13 |
555 |
1.8-3.6 |
1.0 |
0.5-1.5 |
0.08 |
0.08 |
11-14 |
2.0 |
3.0 |
1.2 |
| HBW555XCr16 |
555 |
1.8-3.6 |
1.0 |
0.5-1.5 |
0.08 |
0.08 |
14-18 |
2.0 |
3.0 |
1.2 |
| HBW555XCr21 |
555 |
1.8-3.6 |
1.0 |
0.5-1.5 |
0.08 |
0.08 |
18-23 |
2.0 |
3.0 |
1.2 |
| HBW555XCr27 |
555 |
1.8-3.6 |
1.0 |
0.5-1.5 |
0.08 |
0.08 |
23-30 |
2.0 |
3.0 |
1.2 |
| HBW600XCr35 |
600 |
3.0-5.5 |
1.0 |
1.0-3.0 |
0.06 |
0.06 |
30-40 |
1.0 |
1.5 |
1.2 |
| HBW600XCr20Mo2Cu |
600 |
3.0-5.5 |
1.0 |
1.0 |
0.06 |
0.06 |
18-21 |
1.0 |
1.4-2.0 |
0.8-1.2 |
2. Nihard white Iron:
Handelsname Kurzzeichen W.St.Nr.
Ni-hard 1: ≥ HB500 G-X 330 NiCr 4 2 0.9625
Ni-hard 2: ≥ HB550 G-X 3260 NiCr 4 2 0.9620
Ni-hard 4: ≥ HB600, HB630 G-X 300 NiCrSi 9 5 2 0.9630
G-X 300 NiMo 15 3 0.9635
G-X 260 Cr 27 0.9635
| ISO 21988/JN/ |
HBW |
C |
Si |
Mn |
P |
S |
Ni |
Cr |
| HBW480Cr2 |
480 |
2.5-3.0 |
0.8 |
0.8 |
0.10 |
0.10 |
3.0-5.5 |
1.5-3.0 |
| HBW500Cr9 |
500 |
2.4-2.8 |
1.5-2.2 |
0.2-0.8 |
0.06 |
0.06 |
4.0-5.5 |
8.0-10.0 |
| HBW510Cr2 |
510 |
30.-3.6 |
0.8 |
0.8 |
0.10 |
0.10 |
3.0-5.5 |
1.5-3.0 |
| HBW555Cr9 |
555 |
2.5-3.5 |
1.5-2.5 |
0.3-0.8 |
0.08 |
0.08 |
4.5-6.5 |
8.0-10.0 |
| HBW630Cr9 |
630 |
3.2-3.6 |
1.5-2.2 |
0.2-0.8 |
0.06 |
0.06 |
4.0-5.5 |
8.0-10.0 |
3. Martensitic Cr- Mo Alloy Steel: Hardness: ≥HRC48
4. Pearlitic Cr-Mo Alloy Steel Hardness: HB310-375
5. Heat-resistant Steel Plates.
6. High-temperature Alloy Plates.
7. Hardox Plates:
HARDOX400,HARDOX450, HARDOX500, HARDOX550, HARDOX600,HARDOX630.
8. Bisplate:
BISPLATE 100, BISPLATE 360, BISPLATE 400, BISPLATE 450, BISPLATE 500, BISPLATE 600
Quality Level: As per National Standard & International Standards.
Production Process: Sand ProcessWith proper heat-treatment(quenching and tempering) process to achieve ideal hardness and impact value .
Shape:
Flat Plate, Arc Plate, Waved Plates, Corrugated Plates
Bolted Plates: one-hole, two-holes, three holes, four holes, oval - hole.
Application:
1.Armed plates for clincker silo in cement plants.
2.Wear plates for chutes, material bunkers for port machinery.
3.Material hoppers in steel mills.
4.High abrasion plates for material bin for port maachinery.
5.Wear plates for coal hoppers.
Special Features:
1. We make Cr-Mo Alloy steel and high Cr white iron castings with Sodium Silicate Sand Process and Resin Sand Process.
2. We supply finished alloy steel castings with heat-treatment and machining process.
3. We can produce Alloy Cr-Mo Steel and White Iron castings as per GB/T26651,GB/T 8263-1999,AS2074,AS2027,DIN 1695, AISI,ASTM,JIS G 5153,NF A32401,BS4844.
4. We can recommend suitable material grades of wear parts for you as per your specific working condition.
5. Design of wear plates & Chute Liners.
Width and length of wear plates determines hole pattern, regardless of thickness.
6. Material Selection of Wear Plates & Chute Liners.
Production Process
1. 18-year Foundry Operation Experience.
2. Friendly & High Efficient Technical & Commercial Communication.
3. Professional Export Practices: Have Exported to +60 Overseas Countries.
Our Trade Show
Our booth No. 14-A29-5 in Newcast 2015,Germany
Hall 14, Stand No.A29-5.
Contact Us for further information about products & service:
Mr.John Liu
Project Manager
Tel: 0086-188 0059 6372
Fax: 0086-510-6879 2172
E-mail: cast@ebcastings.com； ebcastings@163.com
Skype ID:julia.zhu26
QQ: 217 039 6403
www.ebcastings.com
Eternal Bliss Alloy Casting & Forging Co.,LTD.
Add.: J-Sci-Tech Park, Binhu District,Wuxi,214122, Jiangsu,China