Product Details:
Payment & Shipping Terms:
|
Material: | Stainless Steel | Grade: | 316L 304L 410L 420 430L |
---|---|---|---|
Shape: | Irregular Shape/Spherical, Powder | Application: | MIM, PM, Filter, 3D Pringting Ect, Maintenance Coatings,Heat Resistance And Durability Coating |
Color: | Gray | Apparent Density: | 2.9-3.1 |
Technology: | Water Atomized | Performance: | Corrosion Resistance Heart Resistance |
Quality Control: | 100% Inspected | Service: | OEM ODM |
Factory Supply 316L 304L 410L 420 430L 17-4PH Alloy Powder Stainless Steel Powder
316l Stainless steel powder is widely used in powder silver sintering, pressing, metal injection molding,
NO.:
|
HR304(L)
|
HR316(L)
|
HR174PH
|
Production Process
|
Atomized
|
Atomized
|
Atomized
|
Grade:
|
304(L)
|
316(L)
|
17-4PH
|
Density
|
app.4.1-4.5
tap.>4.9 g/cm3 |
app.4.1-4.5
tap.>4.8 g/cm3 |
app.4.1-4.5
tap.>4.8 g/cm3 |
Hardness
|
34.5HRC
|
36HRC
|
35HRC
|
Size
|
150um
|
150um
|
150um
|
75um
|
75um
|
75um
|
|
45um
|
45um
|
45um
|
|
15um
|
15um
|
15um
|
|
Content
|
Cr:18-20
Ni:8-12 C:0.08(0.03) Si:1max Mn:2max Fe:bal. |
Cr:16-18
Ni:10-14 Mo:2-3 C:0.08(0.03) Si:1max Mn:2max Fe:bal. |
Cr:15.5-17.5
Ni:3-5 Nb:0.15-0.45 Cu:3-5 C:0.07 Si:1max Mn:1max Fe:bal. |
Applications
|
MIM part weight:0.03-200g
Apparent relative density>95% Sinter density>7.6g/cm3 sinter temperature:1360-1380c Shrinkage rate:1.18 |
MIM part weight:0.03-200g
Apparent relative density>95% Sinter density>7.8g/cm3 sinter temperature:1360-1380c Shrinkage rate:1.18 |
MIM part weight:0.03-200g
Apparent relative density>95% Sinter density>7.8g/cm3 sinter temperature:1360-1380c Shrinkage rate:1.18 |
Name of product | Purity | Particle Size | Chemical Composition | Use |
Stainless steel powder 304 |
Mn:2.0, Cr:18-19, Ni:8-11 |
100mesh/ 200mesh/ 300mesh |
C≤0.07 , Si≤1.0 , Mn≤2.0 , Cr:18.0-19.0, Ni:8.0-11.0, S≤0.03, P≤0.035 |
Maintenance coatings, Heat resistance and durability coating |
Name of product | Purity | Particle Size | Chemical Composition | Use |
Stainless steel powder 316L |
Cr:16-18% Ni:9-13% Si<2% |
100mesh, 200mesh, 300mesh, 15-53um |
Ni:9-13% Si<2% C<0.03% Mo<2% O<0.3% |
Maintenance coatings, heat resistance and durability coating |
Advantage of Stainless Steel Powder:
1. Even powder composition, less impurities.
2. High sphericity.
3. Low oxygen content.
4. Good flowability.
5. High loose density, high tap density.
6. Less hollow powder, less satellite powder.