Product Description:
1. Material: high chromium cast iron;
2. Wear plate thickness: 15mm, 20mm, 15mm, 30mm, 32mm, 40mm, 50mm, 60mm, 80mm, 100mm,
200mm, 500mm, 1000mm, etc., customized by customers;
3. Shape: flat, curved, corrugated, etc., customized by customers;
The sand casting process is used to produce high-chromium cast iron wear-resistant liners.
Do quenching and tempering treatment to achieve better wear performance.
Chemical Composition:
Reference Standard
(ISO 21988-2005) |
Nominal Chemical Composition (W%) |
Eqv. Standards |
| C |
Si |
Mn |
Ni |
Cr |
Mo |
Cu |
P |
S |
ISO 21988/JN/
HBW555XCr13 |
1.8-3.6 |
≤1.0 |
0.5-1.5 |
≤2.0 |
11.0-14.0 |
≤3.0 |
≤1.2 |
≤0.08 |
≤0.08 |
EN-GJN-HV600(XCr11)
ASTM A532 12% Cr |
ISO 21988/JN/
HBW555XCr16 |
1.8-3.6 |
≤1.0 |
0.5-1.5 |
≤2.0 |
14.0-18.0 |
≤3.0 |
≤1.2 |
≤0.08 |
≤0.08 |
EN-GJN-HV600(XCr14)
ASTM A532 15% Cr-Mo
AS 2027 CrMo 15 3
G-X 300 CrMoNi 15 2 1 |
ISO 21988/JN/
HBW555XCr21 |
1.8-3.6 |
≤1.0 |
0.5-1.5 |
≤2.0 |
18.0-23.00 |
≤3.0 |
≤1.2 |
≤0.08 |
≤0.08 |
EN-GJN-HV600(XCr18)
ASTM A532 20% Cr-Mo
AS 2027 CrMo 20 1
G-X 260 CrMoNi 20 2 1 |
ISO 21988/JN/
HBW555XCr27 |
1.8-3.6 |
≤1.0 |
0.5-2.0 |
≤2.0 |
23.0-30.0 |
≤3.0 |
≤1.2 |
≤0.08 |
≤0.08 |
EN-GJN-HV600(XCr23)
ASTM A532 25% Cr-Mo
AS 2027 Cr27 LC & Cr27 HC
G-X 260 Cr27 |
ISO 21988/JN/
HBW600XCr35 |
3.0-5.5 |
≤1.0 |
1.0-3.0 |
≤1.0 |
30.0-40.0 |
≤1.5 |
≤1.2 |
≤0.06 |
≤0.06 |
AS 2027 Cr35 |
ISO 21988/JN/
HBW600XCr20Mo2Cu |
2.6-2.9 |
≤1.0 |
≤1.0 |
≤1.0 |
18.0-21.0 |
1.4-2.0 |
0.8-1.2 |
≤0.06 |
≤0.06 |
AS 2027 CrMoCu 20 2 1
|